SIO-2 Clay
3D Printing Clay - White Grogged Stoneware
High fire white body with 40% impalpable grog 0-0.2 mm, adapted for 3D printing. Its particular white ivory colour after firing is much appreciated and provides an excellent ware for glazes and colouring oxides. Besides, its characteristics offer an excellent behaviour during drying and firing. Available in extruded body with the ideal humidity for 3D printing. Presented in a practical cylindrical format with double packaging. 5kg.
Firing range: 1240-1300ºC
Biscuit Temperature: 10000C
Water Content: 22%
Plasticity (IP Atterburg): 16
Calcium Carbonate CaC03: 0%
Drying Shrinkage: ~8.0%
Firing Shrinkage 13000C: 7.0%
Porosity (water absorption) 13000C: 0%
Dry Bending Strength: 3.0N/mm2
Fired Bending Strength 10500C: 51.0N/mm2